当前位置: 首页 > 文章 > 粘土基微孔陶瓷渗灌灌水器制备与性能优化 农业机械学报 2015,46 (4) 183-188
Position: Home > Articles > Preparation and Performance Optimization of Clay-based Porous Ceramics Used in Subsurface Irrigation Transactions of the Chinese Society for Agricultural Machinery 2015,46 (4) 183-188

粘土基微孔陶瓷渗灌灌水器制备与性能优化

作  者：
蔡耀辉;吴普特;朱德兰;李向明;张林;陈俊英
单  位：
西北农林科技大学中国旱区节水农业研究院;西北农林科技大学水利与建筑工程学院
关键词：
渗灌;灌水器;微孔陶瓷;粘土;炉渣;开口孔隙率
摘  要：
提出了一种渗灌用粘土基微孔陶瓷的低成本制备工艺,通过对比不同制备工艺对粘土基微孔陶瓷的抗弯强度、线收缩率和开口孔隙率的影响规律,筛选出综合具有较高抗弯强度、较小线收缩率和较高开口孔隙率微孔陶瓷的最佳制备工艺。研究表明:烧结温度及炉渣的掺量和粒径对粘土基微孔陶瓷的物相成分、抗弯强度、线收缩率、开口孔隙率和微观结构有较大影响。其中,烧结温度为1 075℃,炉渣掺量质量分数为10%~30%的粗颗粒粘土基微孔陶瓷具有9.0~11.0 MPa的抗弯强度、3.8%~4.7%的线收缩率和36.8%~44.8%的开口孔隙率,是制备渗灌灌水器的理想材料。
译  名：
Preparation and Performance Optimization of Clay-based Porous Ceramics Used in Subsurface Irrigation
作  者：
Cai Yaohui;Wu Pute;Zhu Delan;Li Xiangming;Zhang Lin;Chen Junying;College of Water Resources and Architecture Engineering,Northwest A&F University;Institute of Water Saving Agriculture in Arid Areas of China,Northwest A&F University;
关键词：
Subsurface irrigation Irrigation emitter Porous ceramic Clay Slag Open porosity
摘  要：
Subsurface irrigation has been realized by burying pots,pitchers and subsurface porous pipe,but the present preparation process of porous ceramics could not meet the performance requirements of subsurface irrigation emitters.A new preparation process of clay-based porous ceramics used for subsurface irrigation with minimal cost was explored.The effects of the preparation process(shirking temperature,contents and particle size of slag in the green body) on flexural strength,linear shrinkage and open porosity of porous ceramic were discussed.Finally,the optimal preparation process of porous ceramic with high flexural strength,low linear shrinkage and elevated open porosity were selected.The results showed that the sintering temperature and the contents and particle size of slag in the green body were three key factors influencing the properties of porous ceramics.When sintering temperature was1 075℃ along with content of slag in the green body between 10% and 30%,the porous ceramics showed the best performance with maximum particle size of 0.613 mm.Flexural strength of porous ceramic was 9.0 ~ 11.0 MPa with open porosity of 36.8% ~ 44.8% and the linear shrinkage was 3.8% ~4.7%.Therefore,the clay-based porous ceramic could be the appropriate material for subsurface irrigation emitter.

相似文章

导出引用
计量
文章访问数: 8
HTML全文浏览量: 0
PDF下载量: 0

所属期刊

推荐期刊

友情链接Friendly link
农业信息研究所Agricultural information institute 农业智能知识服务平台Agricultural intelligent knowledge service platform 农业学术服务平台Agricultural Knowledge Service System 中国知网CNKI 维普网VIP 万方WANFANG DATA
联系我们Contact us

电话Tell：010-82109652-808

邮箱E-mail：agrijournal@caas.cn

服务Service
关于我们About us 意见建议Opinions and suggest
版权说明Copyright
单位：中国农业科学院农业信息研究所 中国农学会 © 2017中国农业科学院农业信息研究所 ICP备案号：京ICP备09089781号-46