Position: Home > Articles > Effects of Inorganic Magnesium-aluminium Hydroxide Flame Retardant on Fire Resistance Properties of Medium Density Fiberboard
Journal of Northwest Forestry University
2018
(2)
203-208
无机氢氧化镁铝阻燃剂对中密度纤维板阻燃性能的影响
作 者：
兰平;杨蕊;李维刚;计颖
单 位：
南京林业大学材料科学与工程学院;江苏苏林木业有限公司;承德市工程建设质量监督站
关键词：
无机复合阻燃剂;中密度纤维板;锥形量热仪;阻燃性能;氢氧化镁;氢氧化铝
摘 要：
采用共沉淀法制备无机氢氧化镁(MH)和氢氧化铝(ATH)复合阻燃剂,并将它和ATH分别用于压制阻燃中密度纤维板,探讨无机金属氢氧化物阻燃剂对中密度纤维板燃烧过程中的热释放性能、质量变化、烟释放性能和烟气毒性的影响。结果表明,添加无机氢氧化物的MDF的点燃时间延长;热释放速率和热释放量减小;MDF燃烧过程中质量损失速率降低,残余物质量增多;烟释放量明显减小,烟气中CO_2和CO的生成速率降低,表现出显著的阻燃抑烟效果。与单一ATH相比,无机氢氧化镁铝复合阻燃剂体系中的MH和ATH具有协同阻燃效果,能更有效地降低热量释放和烟释放,提高阻燃效率,减少阻燃剂的用量。
译 名：
Effects of Inorganic Magnesium-aluminium Hydroxide Flame Retardant on Fire Resistance Properties of Medium Density Fiberboard
作 者：
LAN Ping;YANG Rui;LI Wei-gang;JI Ying;College of Materials Science and Engineering,Nanjing Forestry University;Jiangsu Sulin Wood Industry Co.,Ltd.;Chengde Engineering Construction Quality Supervision Station;
关键词：
inorganic composite fire retardant;;MDF;;cone calorimeter;;fire resistance property;;magnesium hydroxide;;aluminium hydroxide
摘 要：
The inorganic magnesium-aluminium hydroxide composite flame retardant was prepared by coprecipitation method.Then flame retardant medium density fiberboard(MDF)was pressed using magnesium-aluminium hydroxide composite and aluminium hydroxide(ATH)as flame retardant,respectively.Effects of different inorganic metal hydroxide on heat release performace,mass loss,smoke performance and toxicity of MDF were discussed.The results showed that the ignition time of flame retardant MDF prolonged,the heat release rate and the total heat release decreased,the mass loss rate declined during combustion and the mass of residue increased after combustion,the smoke release and the production of CO2 and CO in flue gas decreased.It showed significant flame retardant and smoke suppression effects.Compared to ATH,the magnesium hydroxide(MH)and ATH had synergisitic flame retardant effect in inorganic hydroxide compound system.It could more effectively reduce the heat and smoke release of MDF,improve the fire resistance properties and reduce the dosage of flame retardant.