当前位置: 首页 > 文章 > 铝-木复合材料抗弯性能预测与分析 浙江农林大学学报 2017,34 (1) 1-6
Position: Home > Articles > Bending performance of wood-aluminum composites:prediction and analysis Journal of Zhejiang A&F University 2017,34 (1) 1-6

铝-木复合材料抗弯性能预测与分析

作  者：
俞友明;王聪;蔡智勇;卢克阳
单  位：
美国农业部林务局;浙江农林大学;中国林业科学研究院
关键词：
木材科学与技术;铝合金薄板;定向刨花板;弯曲性能;层合理论;预测模型
摘  要：
将铝合金薄板和定向刨花板(OSB)以层叠方式复合得到新型铝-木复合材料(WAC),对不同组坯的铝-木复合材料抗弯性能进行研究,通过三点弯曲加载试验得到铝-木复合材料弯曲破坏形式和抗弯弹性模量,运用经典层合理论建立抗弯弹性模量预测模型,并进行验证。结果表明:将铝合金薄板叠加在最外层的铝-木复合材料结构荷载能力有很大提高,并且纵向弹性模量(MOE)提高了156.55%,横向弹性模量提高了192.79%。考虑胶层影响,在经典层合模型的基础上对铝-木复合材料的弹性模量进行预测,所得预测值和试验值之间相对误差在10%以内。可见经典层合模型可以很好预测铝-木复合材料的弹性模量,铝-木复合材料有着良好的抗弯性能,将铝合金薄板叠加在最外层的结构是最为合理的。
译  名：
Bending performance of wood-aluminum composites:prediction and analysis
作  者：
YU Youming;WANG Cong;CAI Zhiyong;LU Keyang;School of Engineering, Zhejiang A & F University;Forest Products Laboratory,United States Department of Agriculture;Key Laboratory of Wood Science and Technology of State Forestry Administration, Research Institute of Wood Industry, Chinese Academy of Forestry;
关键词：
wood science and technology;;aluminum alloy sheets;;orient strand board;;warping performance;;laminated theory;;predicted model
摘  要：
To research bending behavior of wood-aluminum composites(WAC)and the effect of stacking sequences, orient strand boards(OSB) were laminated with aluminum alloy sheets by different stacking sequencesto manufacture WACs. Then, the bending modulus of elasticity(MOE) and bearing capacity of the WAC were determined using a three-point bending test. Next, a prediction model was established from classical laminated plate theory and validated based on the effect of the glue line. Experimental results indicated that WAC with the structure locating the aluminum alloy sheeton the surface showed the best bending performance.The peak load of WAC, which composite the aluminum alloy sheeton the surface, was 2-fold greater than OSB.In contrast with OSB, the bending MOE for the aluminum alloy sheeton the surface increased 156.55% along the parallel and 192.79% along the perpendicular. The model based on classical laminated plate theory was precise enough to aim at a theoretical MOE with relative error of less than 10%.

相似文章

导出引用
计量
文章访问数: 11
HTML全文浏览量: 0
PDF下载量: 0

所属期刊

推荐期刊

友情链接Friendly link
农业信息研究所Agricultural information institute 农业智能知识服务平台Agricultural intelligent knowledge service platform 农业学术服务平台Agricultural Knowledge Service System 中国知网CNKI 维普网VIP 万方WANFANG DATA
联系我们Contact us

电话Tell：010-82109652-808

邮箱E-mail：agrijournal@caas.cn

服务Service
关于我们About us 意见建议Opinions and suggest
版权说明Copyright
单位：中国农业科学院农业信息研究所 中国农学会 © 2017中国农业科学院农业信息研究所 ICP备案号：京ICP备09089781号-46