当前位置: 首页 > 文章 > 阴香木材物理力学性质研究 西北林学院学报 2016,31 (5) 271-275
Position: Home > Articles > A Study on the Physical and Mechanical Properties of Cinnamomum burmannii Woods Journal of Northwest Forestry University 2016,31 (5) 271-275

阴香木材物理力学性质研究

作  者：
陈柏旭;黄腾华;韦鹏练;符韵林
单  位：
国际竹藤中心;广西大学林学院;广西壮族自治区林业科学研究院
关键词：
阴香;物理性质;力学性质
摘  要：
研究阴香木材的密度、干缩性、弯曲强度、冲击韧性、硬度等主要物理力学性质。结果表明,基本密度、气干密度(含水率为12%)和全干密度分别为0.501、0.609g/cm3和0.581g/cm3,生材密度为1.215g/cm3,气干密度属于国产木材的中等水平。全干差异干缩和气干差异干缩分别为1.59和1.86,弦向和径向干缩系数分别为0.495和0.362,弦向和径向干缩湿胀差异较大。抗弯强度75.6 MPa,顺纹抗压强度41.19 MPa,冲击韧性43.39kJ/m2,端面、弦面和径面硬度分别为4 789.72、4 390.77N和4 260.19N。阴香木材的综合强度为116.79 MPa,属低等级材。
译  名：
A Study on the Physical and Mechanical Properties of Cinnamomum burmannii Woods
作  者：
CHEN Bai-xu;HUANG Teng-hua;WEI Peng-lian;FU Yun-lin;College of Forestry,Guangxi University;The Guangxi Zhuang Autonomous Region Forestry Research Institute;International Center for Bamboo and Rattan;
关键词：
Cinnamomum burmannii;;physical properties;;mechanical property
摘  要：
The main physical properties of Cinnamomum burmannii woods,including the density,dryshrinkage,bending strength,imapct toughness,hardness,etc.,were studied in this paper.As indicated by the results,the basic density,air-dry density(with a moisture content of 12%)and oven-dry density were0.501,0.609g/cm3 and 0.581g/cm3,respectively,and the raw material density was 1.215g/cm3,the airdry density belonged to the medium grade level.The values of differential shrinkage of oven-dried and airdried wood were 1.59 and 1.86,The radial and tangential shrinkage coefficient were 0.495 and 0.362,indicating that the difference of drying shrinkage and the wetting swelling in radial and tangential directions were significant.The values of bending strength and compressive strength parallel to grain were 75.6MPa and 41.19 MPa.The toughness was 43.39kJ/m2,the values of hardness on cross,tangential and radial surfaces were 4 789.72,4 390.77 Nand 4 260.19 N,respectively.The general strength was 116.79 MPa,thus illustrating that the wood was of low quality.

相似文章

导出引用
计量
文章访问数: 13
HTML全文浏览量: 0
PDF下载量: 0

所属期刊

推荐期刊

友情链接Friendly link
农业信息研究所Agricultural information institute 农业智能知识服务平台Agricultural intelligent knowledge service platform 农业学术服务平台Agricultural Knowledge Service System 中国知网CNKI 维普网VIP 万方WANFANG DATA
联系我们Contact us

电话Tell：010-82109652-808

邮箱E-mail：agrijournal@caas.cn

服务Service
关于我们About us 意见建议Opinions and suggest
版权说明Copyright
单位：中国农业科学院农业信息研究所 中国农学会 © 2017中国农业科学院农业信息研究所 ICP备案号：京ICP备09089781号-46