当前位置: 首页 > 文章 > 椰壳热解活化制备活性炭及其机理研究 安徽农业科学 2017 (26) 140-143
Position: Home > Articles > Study on Preparation and Mechanism of Activated Carbon from Coconut Shell by Method of Pyrolysis and Activation Journal of Anhui Agricultural Sciences 2017 (26) 140-143

椰壳热解活化制备活性炭及其机理研究

作  者：
刘雪梅;檀俊利;林明涛;陈玉平;方羽
单  位：
中国林业科学院林产化工研究所南京科技开发总公司;中国林业科学院林产化学工业研究所
关键词：
椰壳;热解;活化;机理
摘  要：
利用热解活化法制备高吸附性能的椰壳活性炭并对其热解活化机理进行研究。结果表明,在热解活化温度为900℃,保温5 h,升温速率为10℃/min时,可以制备比表面积为1 047.65 m~2/g的椰壳活性炭,其中总孔容为0.51 cm~3/g,微孔孔容为0.44 cm~3/g。该活性炭的碘吸附值为1 302 mg/g,亚甲基蓝吸附值为195 mg/g。结果表明:在不添加任何活化气体或化学试剂的情况下,热解活化制备高吸附性能椰壳活性炭的机理可能是由于热解活化过程中,热解释放气体,造成一部分孔隙;高温下未炭化物芳构化形成石墨微晶,键断裂时释放部分气体;这些气体作为活化剂对椰壳原料进行了自活化,生成一定孔隙;在密闭的情况下,热解产生气体,使得反应器内产生微压力,对孔隙的形成有一定作用。
译  名：
Study on Preparation and Mechanism of Activated Carbon from Coconut Shell by Method of Pyrolysis and Activation
作  者：
LIU Xue-mei;TAN Jun-li;LIN Ming-tao;Nanjing General Company for Science & Technology Development Research Institute of Chemical Industry of Forest products,CAF;Institute of Chemical Industry of Forest Products,CAF;
关键词：
Coconut shell;;Pyrolysis;;Activation;;Mechanism
摘  要：
Activated carbon with high adsorption properties were prepared from coconut shell by pyrolysis and activation,which the mechanism were investigated.The results showed that under the condition of pyrolysis and activation temperature at 900 ℃ for 5 hours with the heating rate 10 ℃/min,the prepared carbon had its surface area was 1 047.65 m~2/g,with total pore volume of 0.51 cm~3/g and micropore volume of 0.44 cm~3/g,with the iodine adorption of 1 302 mg/g and methylene blue adsorption of 195 mg/g.The mechanism of pyrolysis and activation for prepared activated carbon has some aspects without any gas or reagent.Some pore was produced from pyrolysis gas,which as activator was in the role of coconut shell.Under the high temperature uncarbonized material forming microcrystalline graphite,breaking bond when release gas.These gases act as activators to self activate the coconut shell material and produce a certain pore.In the airtight case,micro pressure was produced by pyrolysis gas in the reactor,which has a role to formation of the pore.

相似文章

导出引用
计量
文章访问数: 10
HTML全文浏览量: 0
PDF下载量: 0

所属期刊

推荐期刊

友情链接Friendly link
农业信息研究所Agricultural information institute 农业智能知识服务平台Agricultural intelligent knowledge service platform 农业学术服务平台Agricultural Knowledge Service System 中国知网CNKI 维普网VIP 万方WANFANG DATA
联系我们Contact us

电话Tell：010-82109652-808

邮箱E-mail：agrijournal@caas.cn

服务Service
关于我们About us 意见建议Opinions and suggest
版权说明Copyright
单位：中国农业科学院农业信息研究所 中国农学会 © 2017中国农业科学院农业信息研究所 ICP备案号：京ICP备09089781号-46