Position: Home > Articles > Study on Application of Unavailable Tobacco Leaves in Paper-making Reconstituted Tobacco Journal of Anhui Agricultural Sciences 2014 (27) 290-291+294

不适用烟叶在造纸法再造烟叶中的应用研究

作  者:
杨伟平;何振峰;周军;江文斌;杨紫刚;邱妙文
单  位:
广东省烟草南雄科学研究所;广东省金叶烟草薄片技术开发有限公司;广东烟草韶关市有限公司
关键词:
不适用烟叶;造纸法;再造烟叶
摘  要:
[目的]研究不适用烟叶在造纸法再造烟叶中的应用,丰富不适用烟叶处理途径及造纸法再造烟叶的原料来源。[方法]对不适用烟叶进行不同处理,研究其在造纸法再造烟叶中的可用性,并与常规薄片原料对比,进行原料配方技术研究。[结果]试验得出,不适用烟叶快速烘烤(下二棚)处理后的化学成分和感官质量表现优于晾晒和快速烘烤(脚叶)处理,且这3种处理方式的不适用烟叶原料均可应用到造纸法再造烟叶薄片中,以使用烘烤(下二棚)∶晾晒∶烘烤(脚叶)=5∶3∶2的掺配比例替代一半的云南原料,其样品感官质量表现较好。[结论]研究表明,不适用烟叶通过合理的处理方式和配方比例,可部分替代造纸法再造烟叶的原料。
译  名:
Study on Application of Unavailable Tobacco Leaves in Paper-making Reconstituted Tobacco
作  者:
YANG Wei-ping;HE Zhen-feng;ZHOU Jun;Shaoguan Tobacco Company of Guangdong Province;Nanxiong Tobacco Science Research Institute of Guangdong Province;Guangdong Jinye Tobacco Slice Technology Development Co. Ltd.;
关键词:
Unavailable tobacco leaves;;Paper-making;;Reconstituted tobacco
摘  要:
[Objective]To study the application of unavailable tobacco leaves in paper-making reconstituted tobacco,enrich processing way of unavailable tobacco leaves and raw materials of paper-making reconstituted tobacco. [Method]The usability of unavailable tobacco leaves processed by different ways within paper-making reconstituted tobacco was studied,and the material formulation was researched comparing with conventional tobacco slice material. [Result]The results showed: the chemical compositions and sensory qualities of fast baking sample( lower leaves) are superior than the other two ways,curing or fast baking( bottom leaves). Furthermore,these three kinds material in a different way are fit for application in paper-making reconstituted tobacco. And the best ratio is 5∶3∶2,to replace half material from Yunnan. [Conclusion]In conclusion,the unavailable tobacco leaves,with reasonable settlement and blending ratio,could instead a part of paper-making reconstituted tobacco material.