当前位置: 首页 > 文章 > 水润滑橡胶轴承摩擦试验研究 农业机械学报 2006,37 (2) 136-140
Position: Home > Articles > Experimental Study on Friction and Wear Mechanism between Rubber/nickel Coating on Steel Transactions of the Chinese Society for Agricultural Machinery 2006,37 (2) 136-140

水润滑橡胶轴承摩擦试验研究

作  者:
王优强;王龙;黄丙习;林秀娟;李志文
单  位:
青岛理工大学机械工程学院
关键词:
水润滑;橡胶轴承;橡胶/镀镍钢摩擦副;摩擦磨损
摘  要:
利用水润滑轴承专用橡胶材料/镀镍钢配副,分别在干摩擦、湿润滑以及完全水润滑条件下,在数显式高速环块摩擦磨损试验机上进行摩擦磨损试验研究,并借助SEM分析了在不同润滑条件下水润滑轴承专用橡胶材料/镀镍钢摩擦副的摩擦磨损机理。结果认为干摩擦条件下主要为粘着磨损,湿润滑条件下主要为磨粒磨损,而完全水润滑条件下以边界润滑为主。
译  名:
Experimental Study on Friction and Wear Mechanism between Rubber/nickel Coating on Steel
作  者:
Wang Youqiang Wang Long Huang Bingxi Lin Xiujuan Li Zhiwen (Qingdao Technological University)
关键词:
Water lubrication, Rubber bearings, Rubber/nickel coating pair, Friction and wear
摘  要:
Water lubricated rubber bearings sometimes worked in absent-water conditions. The friction and wear characteristics of the water lubricated rubber/nickel coating pair were tested under dry friction, wet friction and water lubrication condition respectively on the MRH3 high-speed ring-block friction and wear testing machine. The friction and wear mechanism of the rubber/nickel coating pair under different conditions was analyzed with the help of SEM. The results showed that the wear mechanism of the pair was adhesive wear under dry condition, grain wear under wet condition and boundary lubrication under water lubrication.