摘  要：
为探究秸秆类农业废弃物所制备生物炭的稳定性,以玉米秸秆和小麦秸秆为原料,分别在200℃和500℃下制备生物炭,通过元素分析、傅里叶红外光谱分析、热重及差热分析等分别探究了生物炭的理化性质及热稳定性。结果表明:玉米秸秆因木质素含量较小麦秸秆高,相同温度下制备的生物炭的热稳定性更高。NaClO、H_2O_2和KMnO4三种氧化剂对生物炭的氧化结果表明,秸秆类生物炭的抗氧化性不仅与高木质素含量有关,且受矿物保护的影响。尤其是在KMnO4体系中,木质素和纤维素含量低、灰分含量高的麦秆及其生物炭的化学稳定性更强,表现出了与热稳定性不同的规律。此外,较高温度下制备的生物炭表现出较强的抗氧化能力,具有较大的碳封存潜力。
译  名：
Thermal stability and oxidation resistance of biochars derived from corn stalk and wheat stalk
作  者：
ZHAO Jin-feng;CHEN Jing-wen;ZHANG Di;Ghosh Saikat;Faculty of Environmental Science and Engineering, Kunming University of Science & Technology;Yunnan Key Laboratory of Carbon Sequestration and Pollution Controlling;
单  位：
ZHAO Jin-feng%CHEN Jing-wen%ZHANG Di%Ghosh Saikat%Faculty of Environmental Science and Engineering, Kunming University of Science & Technology%Yunnan Key Laboratory of Carbon Sequestration and Pollution Controlling
关键词：
biochar;;crop straw;;thermal stability;;oxidation resistance
摘  要：
The objective of this study is to explore the chemical properties and thermal stability of biochars prepared from corn and wheat stalks, which are agricultural wastes. The biochars were prepared at 200 ℃ and 500 ℃. Physical and chemical properties and thermal sta?bility of the biochars were investigated by elemental analysis, fourier transformed infrared spectroscopy(FTIR), and thermo-gravimetric(TGA-DTA)analysis. The results showed that the relative heat stability of corn stalk biochar was higher than that of wheat stalk biocharprepared at the same temperature, which was attributed to the higher lignin content of the former. In addition, biochars prepared from thesame raw materials at a higher temperature showed better thermal stability due to rise in aromaticity. Oxidation of the biochars by NaClO,H_2 O_2, and KMnO4 was minimal. In addition to a high lignin content, mineral protection in stalk biochars prevented oxidation. Particularly,in the KMnO4 system, the wheat stalk biochar, despite lower lignin content, showed stronger chemical stability due to the high ash content,hence, showing a different mode of thermal stability. Besides, the biochars prepared at higher temperatures exhibited a rise in the antioxi?dant capacity and carbon sequestration potential. This study provides valuable insights regarding the practical application and stability of straw biochars.

相似文章

导出引用
计量
文章访问数: 16
HTML全文浏览量: 0
PDF下载量: 0

所属期刊

推荐期刊

友情链接Friendly link
农业信息研究所Agricultural information institute 农业智能知识服务平台Agricultural intelligent knowledge service platform 农业学术服务平台Agricultural Knowledge Service System 中国知网CNKI 维普网VIP 万方WANFANG DATA
联系我们Contact us

电话Tell：010-82109652-808

邮箱E-mail：agrijournal@caas.cn

服务Service
关于我们About us 意见建议Opinions and suggest
版权说明Copyright
单位：中国农业科学院农业信息研究所 中国农学会 © 2017中国农业科学院农业信息研究所 ICP备案号：京ICP备09089781号-46