当前位置: 首页 > 文章 > 水披覆转印技术对PP、PE木塑材表面装饰 森林工程 2016,32 (5) 40-43
Position: Home > Articles > Surface Decoration of PP,PE Wood-plastic Composites Using the Water Transfer Printing Technology Forest Engineering 2016,32 (5) 40-43

水披覆转印技术对PP、PE木塑材表面装饰

作  者：
蔡莹莹;魏长智;韦双颖
单  位：
东北林业大学材料科学与工程学院
关键词：
木塑复合材;水披覆转印技术;表面装饰;附着力
摘  要：
为了使木塑复合材获得更好的表面装饰效果和良好的附着力,对木塑复合材表面分别喷涂热塑丙烯酸树脂漆和硝基漆两种装饰漆料,再经水披覆转印装饰后比较木塑复合材表面的装饰效果和附着力情况,得出水披覆转印的上膜温度在30~40℃、膜干温度在50~70℃内为宜,转印效果最佳;硝基漆装饰木塑复合材表面附着力情况比热塑丙烯酸树脂漆装饰情况要好,硝基漆在2次装饰时表面附着力可达0级,热塑丙烯酸树脂漆需3次装饰,附着力才可达到0级标准;木塑复合材表面经水披覆转印技术处理后,其装饰效果提高,增加附加值。水披覆转印技术适用于装饰木塑复合材料表面。
译  名：
Surface Decoration of PP,PE Wood-plastic Composites Using the Water Transfer Printing Technology
作  者：
Cai Yingying;Wei Changzhi;Wei Shuangying;College of Material Science and Engineering,Northeast Forestry University;
关键词：
wood-plastic composites;;water transfer printing technology;;surface decoration;;adhesion
摘  要：
In order to obtain better surface decorative effect and good adhesion of wood-plastic composite material,two kinds of decorative paints of thermoplastic acrylic resin paint and lacquer were sprayed on wood-plastic composites surface. The surface decorative effect and adhesion of wood-plastic composite materials were compared between two kinds of decorative paints after water transfer printing. It was concluded that transfer printing effect was better when temperature ranged from 30 to 40℃ for the water transfer printing and from 50 to 70℃ for film drying. Compared with thermoplastic acrylic resin paint,lacquer was better in terms of surface adhesion. Adhesion can reach the standard level 0 when lacquer decorated twice or thermoplastic acrylic resin paint decorated three times. The surface decorative effect of wood-plastic composites was improved after water transfer printing treatment and added value was also enhanced. The water transfer printing technology was proved to be suitable for wood-plastic composites surface decoration in this study.

相似文章

导出引用
计量
文章访问数: 10
HTML全文浏览量: 0
PDF下载量: 0

所属期刊

推荐期刊

友情链接Friendly link
农业信息研究所Agricultural information institute 农业智能知识服务平台Agricultural intelligent knowledge service platform 农业学术服务平台Agricultural Knowledge Service System 中国知网CNKI 维普网VIP 万方WANFANG DATA
联系我们Contact us

电话Tell：010-82109652-808

邮箱E-mail：agrijournal@caas.cn

服务Service
关于我们About us 意见建议Opinions and suggest
版权说明Copyright
单位：中国农业科学院农业信息研究所 中国农学会 © 2017中国农业科学院农业信息研究所 ICP备案号：京ICP备09089781号-46