Position: Home > Articles > Preparation of Large Specific Surface Area Coal-bearing Kaolin by an Acid Activation Method and Its Properties
Journal of Shihezi University(Natural Science)
2014
(3)
366-370
高比表面积煤系高岭土材料的制备及其结构表征
作 者：
李新梅;长山;白孟兰;张冬云;德力格尔;吴哈申
单 位：
内蒙古师范大学化学与环境科学学院/内蒙古自治区功能材料物理与化学重点实验室
关键词：
煤系高岭土;煅烧;化学活化;酸改性;比表面积
摘 要：
高比表面积改性煤系高岭土具有优异的性能,现已被广泛地应用于多种行业。本文以内蒙煤系高岭土为原料,将其高温煅烧制得偏高岭土后,再经盐酸改性用以制备高比表面煤系高岭土材料;通过X射线衍射(XRD)、差热-热重分析(DTA-TGA)和N2吸附-脱附等手段对改性前后煤系高岭土的晶体结构及比表面积进行了表征,实验考察了煅烧温度、煅烧时间、盐酸用量、盐酸浓度及反应时间对煅烧煤系高岭土比表面积的影响,确定了酸改性煤系高岭土的最佳工艺条件;在最佳工艺条件下制备的盐酸改性煤系高岭土材料的比表面积高达465 m2/g。
译 名：
Preparation of Large Specific Surface Area Coal-bearing Kaolin by an Acid Activation Method and Its Properties
作 者：
LI Xinmei;CHANG Shan;Bai Menglan;ZHANG Dongyun;Deligeer;WU Hashen;Inner Mongolia Key Laboratory for Physics and Chemistry of Functional Materials,College of Chemistry and Environmental Science,Inner Mongolia Normal University;
关键词：
Coal-bearing kaolinite;;Calcination;;Chemical activation;;Acid activation;;Surface area
摘 要：
Large specific surface area activated coal-bearing kaolin which has excellent characters is widely used in various industries.In this study,kaolinite material with a large specific surface area was prepared from Inner Mongolia coal-bearing kaolinite by high temperature heat treatment and hydrochloric acid treatment.The crystal structure and specific surface area were characterized by using X-ray diffraction and N2adsorption-desorption.The thermogravimetry analysis(TGA) and differential thermal analysis(DTA) were collected also.The effects of calcination temperature,calcination time,dosage of hydrochloric acid,concentration of hydrochloric acid and acid treatment time on the specific surface area of calcined coal-bearing kaolinite were investigated to determine the optimum condition.The maximum specific surface area of the kaolinite material prepared under the optimum condition was as large as 465 m2/g.