当前位置: 首页 > 文章 > 3种木塑复合材料的耐老化性能比较浙江农林大学学报 2014,31 (1) 117-121

Position: Home > Articles > Surface properties of biomass fiber/polyethylene composites with accelerated ultraviolet weathering Journal of Zhejiang A&F University 2014,31 (1) 117-121

3种木塑复合材料的耐老化性能比较

作者：

胡晗;吴章康;王云;关成;黄伟

单位：

西双版纳华坤生物科技有限公司;西南林业大学材料工程学院

关键词：

天然材料;木塑复合材料;紫外荧光老化;老化性能

摘要：

木塑复合材料的老化性能直接关系其使用寿命和适用范围。使用稻壳、橡胶木锯末和橡胶籽壳分别与回收聚乙烯混合制备木塑复合材料。通过色差分析、红外光谱分析和差示扫描量热法(DSC),研究了3种木塑复合材料经紫外荧光老化后表面颜色、化学成分及结晶度的变化。结果表明,经2 000 h紫外荧光辐照后,处理B(锯末)ΔL和ΔE值为35和30,处理A(稻壳)为40和37,处理C(橡胶籽壳)为45和43;3种材料表面羰基浓度增大,表面氧化程度加深;紫外荧光辐照1 000 h后,处理B(锯末)结晶度由59.21上升到88.44,增加了49.37%;处理A(稻壳)结晶度由63.53上升到94.00,增加了47.96%;处理C(橡胶籽壳)结晶度由55.42上升到98.35,增加了77.46%。图4表1参13

译名：

Surface properties of biomass fiber/polyethylene composites with accelerated ultraviolet weathering

作者：

HU Han;WU Zhangkang;WANG Yun;GUAN Cheng;HUANG Wei;Material Engineering College, Southwest Forestry University;Xishuangbanna Huakun Biological Company;

关键词：

natural material;;wood plastic composites;;ultraviolet accelerating;;aging properties

摘要：

Aging properties of wood-plastic composites are directly related to their application. Currently, rubber wood and rubber seed shell are used in wood-plastic composites has not been reported. Changes on the surface of materials will be tested emphatically. Rice husk, rubber wood fiber, and rubber seed shell were each mixed with high-density polyethylene(HDPE) to make wood-plastic composites. Change in surface color, chemical composition, and degree of crystallinity for the three different materials subjected to ultraviolet(UV) weathering were monitored using color analysis, Fourier transform infrared spectroscopy(FTIR) and differential scanning calorimetry(DSC). Results showed that after 2 000 h of aging, the ΔL and ΔE for rubber wood fiber was 35 and 30, for husks was 40 and 37, and for rubber seed shell was 45 and 43, respectively. Also, the concentration of carbonyl groups on the surface of the three materials increased, and the degree of oxidation was enhanced. After aging 1 000 h, crystallinity of the rubber wood fiber treatment increased from 88.44 to 59.21(49.37%); for the husks treatment it increased from 94.00 to 63.53(47.96%); and for the rubber seed shell treatment it increased from 55.42 to 98.35(77.46%). [Ch, 4 fig. 1 tab. 13 ref.]

相似文章

壳聚糖的生理活性 [] 北方园艺 2012 (9) 164
天然材料在包装设计中的传承与发展 [刘心悦, 刘赛, 王舒琪] 河北农机 2020 (6) 44-45
EPLF强化木地板动态 [管宁] 国际木业 2007,037 (9) 63-64
木材强于钢材 [陈玲] 国际木业 2018,48 (3) 55
广东特色天然材料在大健康产业中的应用现状及发展-以河源市为例 [陈煜, 李娜, 童宗睿, 张舰月, 姚楚旋, 吴志平, 叶有碧, 郑永发, 李普旺, 邵立伟, 黄斌] 热带农业科学 2018 (6)
日本住友公司研发100％天然材料的汽车轮胎 [莫业勇] 世界热带农业信息 2010 (7)
天然有机物包裹控释尿素的养分释放特征及其肥效研究 [王恩飞, 莫海涛, 崔智多, 蒋小姝, 张小勇] 中国农学通报 2012,28 (30) 90-94
天然源材料在农药剂型加工中的研究进展 [时海涛, 徐勇, 张泗达, 吴学民, 徐建富] 中国植保导刊 2022,42 (8) 20-23,36
麻天然材料包装须有符合食品外包装的国标依据设计及应用前景 [彭建祥] 湖南生态科学学报 2014 (3) 59-62

导出引用

计量

文章访问数: 9

HTML全文浏览量: 0

PDF下载量: 0

3种木塑复合材料的耐老化性能比较

相似文章

所属期刊

浙江农林大学学报

推荐期刊

河北农机

国际木业