当前位置: 首页 > 文章 > 纳米羟基磷灰石改性生物炭对铜的吸附性能研究 农业环境科学学报 2017 (10) 2092-2098
Position: Home > Articles > Comparison of copper adsorption onto unmodified and nano-hydroxyapatite-modified wheat straw biochar Journal of Agro-Environment Science 2017 (10) 2092-2098

纳米羟基磷灰石改性生物炭对铜的吸附性能研究

作  者：
朱司航;赵晶晶;楚龙港;尹英杰;陈冲;商建英
单  位：
中国农业大学资源与环境学院
关键词：
纳米羟基磷灰石;小麦秸秆;生物炭;Cu2+;吸附
摘  要：
为了提高生物炭对重金属铜的吸附能力,选取小麦秸秆作为原料,将不同比例纳米羟基磷灰石与秸秆混合均匀,在600℃高温限氧条件下制备了羟基磷灰石改性生物炭材料,比较了生物炭和生物炭改性材料对铜的吸附特性,同时分析了两者间的表面特征等。结果表明:热重分析显示,生物炭表面附着纳米羟基磷灰石可以提高生物炭的热稳定性;扫描电子显微镜分析显示,纳米羟基磷灰石可以较为均匀地附着在生物炭表面,但同时会伴随不同程度的聚集现象;接触角测试结果显示,生物炭表面附着纳米羟基磷灰石可降低其疏水性;生物炭和生物炭改性材料对铜的吸附符合伪二级动力学模型,生物炭改性材料可使铜的吸附速率提高7.69%~130.77%;生物炭和生物炭改性材料对不同浓度的铜吸附符合Langmuir等温吸附模型,对铜的最大吸附量分别为32.65 mg·g~(-1)和57.01 mg·g~(-1)。
译  名：
Comparison of copper adsorption onto unmodified and nano-hydroxyapatite-modified wheat straw biochar
作  者：
ZHU Si-hang;ZHAO Jing-jing;CHU Long-gang;YIN Ying-jie;CHEN Chong;SHANG Jian-ying;College of Resource and Environment, China Agricultural University;Key Laboratory of Plant-Soil Interactions,Ministry of Education;Key Laboratory of Arable Land Conservation(North China), Ministry of Agriculture;
关键词：
nano-hydroxyapatite;;wheat straw;;biochar;;Cu2+;;adsorption
摘  要：
To improve wheat straw biochar′s removal ability of copper from polluted water and soils, wheat straw biochar was modified using nano-hydroxyapatite. The characteristics of unmodified and nano-hydroxyapatite-modified wheat straw biochars were analyzed, and batch and kinetic adsorption experiments were conducted. The results showed that the nano-hydroxyapatite coating was uniformly attached to the surface and improved the thermal stability of the wheat straw biochar. All three concentrations of the nano-hydroxyapatite coating decreased the hydrophobicity of the biochar. The nano-hydroxyapatite coating increased the adsorption rate of copper by 7.69%~130.77%. The maxi-mum adsorption capacity of nano-hydroxyapatite-modified wheat straw biochar increased from 32.65 mg·g~(-1)without coating to 57.01 mg·g~(-1)with 0.5% coating. Copper adsorption onto unmodified and nano-hydroxyapatite-modified wheat straw biochars were well fitted by the pseudo-second-order kinetics and Langmuir adsorption models.

相似文章

导出引用
计量
文章访问数: 11
HTML全文浏览量: 0
PDF下载量: 0

所属期刊

推荐期刊

友情链接Friendly link
农业信息研究所Agricultural information institute 农业智能知识服务平台Agricultural intelligent knowledge service platform 农业学术服务平台Agricultural Knowledge Service System 中国知网CNKI 维普网VIP 万方WANFANG DATA
联系我们Contact us

电话Tell：010-82109652-808

邮箱E-mail：agrijournal@caas.cn

服务Service
关于我们About us 意见建议Opinions and suggest
版权说明Copyright
单位：中国农业科学院农业信息研究所 中国农学会 © 2017中国农业科学院农业信息研究所 ICP备案号：京ICP备09089781号-46