当前位置: 首页 > 文章 > 响应面优化魔芋葡甘聚糖膜力学性能研究 食品科学 2010,31 (10) 95-100
Position: Home > Articles > Response Surface Analysis for Optimization of Mechanical Properties of Konjac Glucomannan Film FOOD SCIENCE 2010,31 (10) 95-100

响应面优化魔芋葡甘聚糖膜力学性能研究

作  者：
陈文平;江贵林;汪超;陈士勇;吕文平;姜发堂
单  位：
湖北工业大学生物工程学院
关键词：
魔芋葡甘聚糖;拉伸强度;响应面分析
摘  要：
水相中溶致魔芋葡甘聚糖(KGM)流延干燥成膜,分析膜的力学特性。筛选并确定KGM质量浓度、制备温度、制备时间、静置时间、干燥温度5个因素的中心组合试验设计,以拉伸强度为考察指标,采用响应面优化KGM膜的制备工艺。结果表明:5个因素对膜的拉伸强度均有显著影响,依次为KGM质量浓度>制备温度>静置时间>干燥温度>制备时间,且最优条件为2.19g/100mLKGM、60.0℃搅拌190min、静置156min、51.1℃干燥。制备的膜表面平整光滑,拉伸强度最佳,耐水性较好。
译  名：
Response Surface Analysis for Optimization of Mechanical Properties of Konjac Glucomannan Film
作  者：
CHEN Wen-ping1,JIANG Gui-lin1,WANG Chao1,2,CHEN Shi-yong1,LU Wen-ping1,JIANG Fa-tang1,2 (1. School of Biological Engineering, Hubei University of Technology, Wuhan 430068, China; 2. Wuhan Licheng Biotechnology Co. Ltd., Wuhan 430074, China)
关键词：
konjac glucomannan;tensile strength;response surface analysis
摘  要：
To achieve optimal mechanical properties of konjac glucomannan (KGM) film prepared by the solution casting method, Plackett-Burman factorial design was used to select the most important ones affecting KGM film tensile strength out of 7 technological parameters and subsequently, the optimal values of selected parameters, namely KGM concentration (X1), stirring time (X2), heating temperature (X3), standing time (X5) and drying temperature (X7), for improved KGM film tensile strength were investigated using response surface analysis based on a 5-variable, 3-level central composite design leading to 46 experiments. Results showed that the above selected parameters all had significant effects on KGM film tensile strength in the decreasing order: X1 > X3 > X2 > X7 > X5 and their optimal values were as follows: KGM concentration 2.19 g/100 mL, heating temperature 60.0 ℃ for 190 min stirring, standing time 156 min and drying temperature 51.1 ℃. The KGM film obtained under such conditions exhibited a smooth regular surface, an optimal tensile strength and good water resistance.

相似文章

导出引用
计量
文章访问数: 8
HTML全文浏览量: 0
PDF下载量: 0

所属期刊

推荐期刊

友情链接Friendly link
农业信息研究所Agricultural information institute 农业智能知识服务平台Agricultural intelligent knowledge service platform 农业学术服务平台Agricultural Knowledge Service System 中国知网CNKI 维普网VIP 万方WANFANG DATA
联系我们Contact us

电话Tell：010-82109652-808

邮箱E-mail：agrijournal@caas.cn

服务Service
关于我们About us 意见建议Opinions and suggest
版权说明Copyright
单位：中国农业科学院农业信息研究所 中国农学会 © 2017中国农业科学院农业信息研究所 ICP备案号：京ICP备09089781号-46