当前位置: 首页 > 文章 > 静电纺CNC增强PMMA纳米复合纤维的制备与性能 福建农林大学学报(自然科学版) 2021 (4) 562-569
Position: Home > Articles > 静电纺CNC增强PMMA纳米复合纤维的制备与性能 Journal of Fujian Agriculture and Forestry University(Natural Science Edition) 2021 (4) 562-569

静电纺CNC增强PMMA纳米复合纤维的制备与性能

作  者：
张彦;倪晓慧;王栋;程万里;韩广萍
单  位：
东北林业大学生物质材料科学与技术教育部重点实验室/木质新型材料教育部工程研究中心
关键词：
静电纺丝;纤维素纳米晶体;聚甲基丙烯酸甲酯;纳米复合纤维;力学性能;
摘  要：
为了提高聚甲基丙烯酸甲酯（polymethyl methacrylate, PMMA）纳米纤维的力学强度,以纳米纤维素晶体（cellulose nanocrystals, CNC）为增强体,采用静电纺丝技术制备了CNC/PMMA纳米复合纤维,考察了CNC添加量对CNC/PMMA纳米复合纤维的微观形貌、力学性能和热学性能的影响,结果表明CNC可均匀分布在电纺液和PMMA基体中,所制备的CNC/PMMA纳米复合纤维表面光滑,形貌规整.随着CNC添加量的增大,纳米复合纤维直径从1.37μm减小到0.48μm,表明添加CNC可显著提高CNC/PMMA纳米复合纤维的力学性能.随着CNC添加量的增加,拉伸强度呈现先增大后减小的趋势;当CNC添加量为16%时,CNC/PMMA纳米复合纤维的力学性能最优,最大拉伸强度为0.31 MPa,比纯PMMA纳米纤维提高107%.此外,添加CNC可小幅提高CNC/PMMA纳米复合纤维的玻璃化转变温度和热稳定性.
作  者：
ZHANG Yan;NI Xiaohui;WANG Dong;CHENG Wanli;HAN Guangping;Key Laboratory for Bio-based Material Science and Technology of Ministry of Education/Engineering Research Center for Advanced Wooden Materials of Ministry of Education, Northeast Forestry University;
关键词：
electrospinning;;cellulose nanocrystals;;polymethylmethacrylate;;nanocomposite fiber;;mechanical property
摘  要：
In order to enhance the mechanical strength of polymethylmethacrylate(PMMA) nanofiber, CNC/PMMA nanocomposite fiber was prepared using cellulose nanocrystals(CNC) as the reinforcement via electrospinning. The effects of CNC loading on the morphology, mechanical and thermal properties of CNC/PMMA nanocomposite fibers were investigated. The results revealed that CNC could be evenly distributed in the electrospinning solution and PMMA matrix, and the prepared CNC/PMMA nanocomposite fiber had smooth surface and regular morphology. As CNC loading increased, the average diameter of nanocomposite fiber decreased from 1.37 μm to 0.48 μm. The addition of CNC significantly improved the mechanical properties of CNC/PMMA nanocomposite fiber. With the increase of CNC content, the tensile strength first increased and then decreased. When CNC loading reached 16%, the tensile strength of nanocomposite fibers peaked at 0.31 MPa, which was improved by 107% compared with the pure PMMA nanofiber. In addition, the glass transition temperature and thermal stability of nanocomposite fiber were slightly improved.

相似文章

导出引用
计量
文章访问数: 4
HTML全文浏览量: 0
PDF下载量: 0

所属期刊

推荐期刊

友情链接Friendly link
农业信息研究所Agricultural information institute 农业智能知识服务平台Agricultural intelligent knowledge service platform 农业学术服务平台Agricultural Knowledge Service System 中国知网CNKI 维普网VIP 万方WANFANG DATA
联系我们Contact us

电话Tell：010-82109652-808

邮箱E-mail：agrijournal@caas.cn

服务Service
关于我们About us 意见建议Opinions and suggest
版权说明Copyright
单位：中国农业科学院农业信息研究所 中国农学会 © 2017中国农业科学院农业信息研究所 ICP备案号：京ICP备09089781号-46